Copper Round Rod Weight Calculator
Calculate the weight of Copper Round Rod by entering your dimensions. The density of Copper is 0.324 lb/in³ (8968 kg/m³). Use this calculator for quick stock weight estimates in your CNC machining projects. Accurate weight calculations are essential for shipping quotes, material cost estimation, fixturing load analysis, and structural design verification. The theoretical weight formula assumes a uniform cross-section and standard alloy density; actual weights may differ slightly by grade and mill tolerance. Weight data is calculated using the standard volumetric formula multiplied by the material density constant shown above.
Material Properties
| Material | Copper |
| Shape | Round Rod |
| Density | 0.324 lb/in³ / 559.9 lb/ft³ / 8968 kg/m³ |
| Example Weight | 3.054 lb / 1.385 kg |
Compare Materials — Round Rod
| Material | Weight (lb) | Weight (kg) |
|---|---|---|
| Aluminum | 0.919 | 0.417 |
| Titanium | 1.517 | 0.688 |
| Cast Iron | 2.45 | 1.112 |
| Steel | 2.67 | 1.211 |
| Stainless Steel | 2.71 | 1.229 |
| Brass | 2.889 | 1.31 |
| Copper (current) | 3.054 | 1.385 |
Sourcing and Use Notes
C110 ETP (electrolytic tough pitch) copper is the standard electrical conductor stock — minimum 99.9% Cu with excellent conductivity but poor machinability because of its gummy chip. C145 tellurium copper alloys in a small amount of tellurium to break chips cleanly, sacrificing about 5% conductivity for production-line machinability. Copper oxidizes quickly in shop air; bare stock will develop a brown-to-green patina within weeks, so order soft-temper coiled sheet or clean and protect finished parts within days. Copper accepts silver brazing readily and is ductile enough for tight bend radii without annealing.
Round bar is the universal turning stock — used for shafts, dowels, pins, threaded rod blanks, and any rotationally symmetric part. Cold-drawn round bar typically holds h9 concentricity (about ±0.05 mm on 25 mm diameter), which is the right starting point for parts that will be finish-turned. For ground-and-polished shaft applications (linear motion shafting, hydraulic cylinder rods) buy h7 ground bar to save a turning operation. Hot-rolled round is cheaper but loose on roundness and surface finish — appropriate only for stock that will be fully machined on every diameter.
Common Applications
Copper Round Rod is a standard stock form used in structural frames, machine bases, brackets, and fabricated components. Its consistent cross-section simplifies weight-per-foot calculations and material takeoffs for procurement and shipping cost estimates. Engineers and machinists rely on theoretical weight data during the quoting and planning stages before final parts are produced. For large orders or weight-critical designs, request certified mill test reports (MTRs) to confirm actual density and alloy composition.
Sourcing and Weight Tolerance Note
This weight is based on the theoretical density of Copper. Mill tolerances (ASTM A6 allows ±2.5% on cross-sectional area for structural shapes) and surface treatments (anodizing, plating, painting) may add 1–3% to actual shipped weight. Order 5–10% material overage to account for saw kerfs and offcuts. Always verify actual material density with your supplier's material test report (MTR) for critical structural or load-bearing applications. Compare weights across materials using the comparison table above to make informed material selection decisions for your project.